2001年大修期间,对三塔进行了全面检验,分析原因后采取有效错施,解决了表面裂纹问题,至今未出现大修以前的损坏现象。
During the overhaul period in 2001, an all-sided inspection was made to the three towers, causes were analysed, and measures were taken, the problem of surface cracks have been solved.
采用化学分析、金相检验和显微硬度梯度试验等方法对油压机柱塞表面淬火交界处裂纹进行了分析。
The crack in quenching boundary of the hydraulic press plunger surface was analyzed by means of chemical composition analysis, microstructure examination and microhardness testing.
在上海炼油厂预加氢反应器投用前的内外部检验中,发现了大量的焊缝表面裂纹和内部埋藏裂纹。
On overall inspection of interior and exterior of pre-hydrogenating reactor of Shanghai Oil Refinery Factory, large cracks was found on the surface of weld and inside of the weld.