抗弯强度，是指材料抵抗弯曲不断裂的能力，主要用于考察陶瓷等脆性材料的强度。一般采用三点抗弯测试或四点测试方法评测。其中四点测试要两个加载力，比较复杂；三点测试最常用。其值与承受的最大压力成正比。抗弯强度（弯曲强度）bendingstrength
misc. bending strength ; bending resistance
Correspondingly, the wrapping materials have smaller effects on the tensile strength, and the species of the rattan cane have smaller effect on the bending strength.
缠结材料对抗拉强度影响显著程度相对较小,基材对抗弯强度影响显著程度相对较小。
参考来源 - 藤家具质量评定及检验方法的研究Flexural strength and fracture toughness of SiO2-AlN composites with 30 vol% AlN particles sintered at 1400℃ reached 200 MPa and 2.96 MPa*m1/2 respectively.
1400℃下热压烧结的30 vol%AlN-SiO2复合材料的抗弯强度和断裂韧性分别达200 MPa和2.96 MPam1/2。
参考来源 - SiO2The result illustrates that the residual thermal stress of the TZ-3Y20A/Mo multiplayer composite is less than the flexure strength of TZ-3Y20A ceramic at the same experimental condition when the layer number and layer thickness' ratio exceeds 27 and 2 respectively.
结果表明，当叠层材料层数和层厚比分别超过27和2时，计算得到的残余应力小于TZ-3Y20A陶瓷的抗弯强度。
参考来源 - TZThe bulk density of this material is 2.71 g/cm3, the bending strength is 120MPa, the dielectric constant and the dielectric loss at 1MHz are 8.6 and 1.27×10-3 respectivly.
烧结试样的体积密度为2.71g/cm3,抗弯强度为120MPa;在1MHz的测试频率下,其介电常数为8.6,介电损耗为1.27×10-3。
参考来源 - CBS/AlThe maximum values of the fracture toughness and the flexural strength can be obtained when the amount of WC particles is 4wt. % and 8wt.
适量WC颗粒的添加可以提高纳米Si3N4陶瓷的断裂韧性和抗弯强度，其最大值分别在WC添加量为4wt.％和8wt.％时获得。
参考来源 - 纳米SiThe relations between sintering processes and microstructure, densification are analyzed. Influences of machining on the flexure strength of Si3N4 are discussed.
本文研究了热压烧结工艺、气压烧结工艺对Si_3N_4显微结构、致密化的影响，分析了烧结工艺和显微结构、致密化的关系，讨论了机械加工对Si_3N_4抗弯强度的影响。
参考来源 - 制备工艺与氮化硅显微结构及性能的相关性Welding amount had little effect on appearance, deformation, microstructure, tensile strength, bend strength, hardness and fracture characters.
焊接次数对焊缝外观、焊后变形、焊缝组织、抗拉强度、抗弯强度以及硬度的影响都很小,断口形貌一致。
参考来源 - 5A06铝合金多次搅拌摩擦焊接头组织及力学性能研究The transverse-repture strength of the porous metal bonded diamond segments was measured by three-point bend to fail test. We selected the 40/50 diamond according the results.
测量了试样与节块抗弯强度。
参考来源 - 多孔金属结合剂金刚石砂轮的制备及应用研究③2.5%Povidone Iodine spraying disinfection adversely affected the bending resistance(P＜0.01).
③2.5%的碘伏喷雾后,两种石膏模型的抗弯强度值有极显著性差异(P＜0.01)。
参考来源 - 石膏模型消毒后物理性能及消毒效果的比较研究·2,447,543篇论文数据，部分数据来源于NoteExpress
探讨了核化温度与抗弯强度之间的关系。
The relationship between nucleation temperature and flexural strength was investigated.
此外，还对抗弯强度试样的断口进行了分析。
Additionally, the fracture surfaces of bending strength specimen were also explained.
随着温度降低，玻璃板的抗弯强度测定值增加。
It is found that the bending strength of gauge glass increases when the temperature decreases.