得出了完全再结晶温度和开始过烧温度。
The fully recrystallization temperature and the on-set overheated temperature have also been obtained.
试验结果表明,在一定的温度下,铌锆合金丝材达到完全再结晶的最佳总加工率在82%附近。
The best general working rate that Nb-1Zr wire was recrystallized completely was about 82% at a given annealing temperature.
高温小变形时容易发生不完全再结晶,造成晶粒粗大且不均匀,在随后的轧制过程中很难消除。
Small deformation in high temperature is easy to cause incomplete recrystallization and bulky and uneven grain. It is hard to eliminate them in subsequent rolling process.