得出了完全再结晶温度和开始过烧温度。
The fully recrystallization temperature and the on-set overheated temperature have also been obtained.
试验结果表明,在一定的温度下,铌锆合金丝材达到完全再结晶的最佳总加工率在82%附近。
The best general working rate that Nb-1Zr wire was recrystallized completely was about 82% at a given annealing temperature.
高温小变形时容易发生不完全再结晶,造成晶粒粗大且不均匀,在随后的轧制过程中很难消除。
Small deformation in high temperature is easy to cause incomplete recrystallization and bulky and uneven grain. It is hard to eliminate them in subsequent rolling process.
在上面概述的方法之后将产生显示出良好强度和伸长率的细晶粒、完全再结晶、模压淬火的产品。
Following the method outlined above will produce a fine-grained, fully recrystallized, press quenched product that demonstrates good strength and elongation.
结果表明:由于发生了相对完全的二次再结晶,横向轧制板材能得到理想的终态组织。
The results show that transverse rolling sheet could create comparatively perfect structure due to the occurrence of secondary recrystallization.