The results show that, under the middle or low impact, comparedwiththehighmanganesequenchedat1080℃ , the hardness of the medium manganese tempered at 600℃ is higher ,and the resistance to wearing is better. Though the impact tenacity is lower, it canreach1.52MJ/m2and meetthedemand.
结果表明,600℃回火处理后中锰钢的硬度比高锰钢高,在中、低冲击载荷作用下的耐磨性比高锰钢好,冲击韧性不及高锰钢,但也到达1.52MJ/m~2,能够满足现场生产需要。
参考来源 - 中锰钢在中、低冲击工作条件下的开发与应用·2,447,543篇论文数据，部分数据来源于NoteExpress
通过自制的冲击腐蚀磨损试验机，施加不同极化电位对高锰钢在矿浆介质中的冲击腐蚀磨损行为进行了试验研究。
Effect of polarization potential on the corrosion-wear behavior of high manganese steel in ore slurry was investigated by a self-made impact corrosive-wear tester.
针对传统上高锰钢作为履带板材料在实际应用中的不足，研究了一种新型的铸造m - B低合金高强度耐磨钢。
A kind of new M-B low-alloy wear resistance steel with high strength has been studied to overcome the deficiency of traditional high-manganese steel used in making grippad.
针对用国标规定的稀硫酸溶解试样、钼蓝光度法测定高锰钢中的硅存在结果偏低的问题，试验验证了用硝酸溶样能保证测定结果的准确性。
The GB stipulates that high manganese steel should be dissolved by rare sulphuric acid, the silicon in the solution should be determined by the molybdenum blue photometric method.