Measures controlling the morphology of inclusions and reducing the degree of segregation was proposed.
提出了有效控制夹杂物形态、降低偏析程度的技术措施。
The results showed that the solid liquid phase zone, temperature interval and segregation degree may be obviously enlarged with increasing s content so as to reduce the hot plasticity of the alloy.
结果表明,随着S含量的增加,导致固液两相区、温度范围和偏析程度明显加大,引起合金的热塑性降低。
Based on pot tests with different carbon profile in sinter-bed, it is found that suitable degree of carbon segregation in three-layer is 0.4%.
通过不同燃料偏析程度的烧结杯试验,说明酒钢酸性球团烧结工艺在上中下三层的合理燃料偏析程度是0.4%。