Measures controlling the morphology of inclusions and reducing the degree of segregation was proposed.
提出了有效控制夹杂物形态、降低偏析程度的技术措施。
The results showed that the solid liquid phase zone, temperature interval and segregation degree may be obviously enlarged with increasing s content so as to reduce the hot plasticity of the alloy.
结果表明,随着S含量的增加,导致固液两相区、温度范围和偏析程度明显加大,引起合金的热塑性降低。
Based on pot tests with different carbon profile in sinter-bed, it is found that suitable degree of carbon segregation in three-layer is 0.4%.
通过不同燃料偏析程度的烧结杯试验,说明酒钢酸性球团烧结工艺在上中下三层的合理燃料偏析程度是0.4%。
Adoption of speeded changing could reduce the degree of carbide segregation more than 3 grades whereas repeated upsetting and drawing-out could only reduce 1-1.5 grades.
本文通过大量试验和机理的研究,高速钢锻件经过反复镦拔。只能降低炭化物偏析度1~1.5级。
The measurement of DMTA and SEM was used to study the morphology and structure of the cured epoxy, identifying the degree of phase segregation and the effect of toughening in the cured epoxy.
以液体聚硫聚脲齐聚物来增韧环氧-聚酰胺体系,用DMTA和SEM研究了固化后环氧树脂的形态结构、相分离程度和增韧效果。
Regressive analysis shows segregation index has maximal relationship with water ratio in secondary cooling, and has low relationship with superheat degree of steel.
回归分析表明偏析指数与二冷比水量的相关性最大,而与钢水过热度的相关性不强。
Regressive analysis shows segregation index has maximal relationship with water ratio in secondary cooling, and has low relationship with superheat degree of steel.
回归分析表明偏析指数与二冷比水量的相关性最大,而与钢水过热度的相关性不强。