通过对其疲劳性能的实验研究,发现裂纹扩展速率的大小及刚度的下降与加载的最大循环应力密切相关的规律。
The fatigue properties were researched and found that the crack propagation velocity and the decline of rigidity were related to the maximum cycle stress.
木文研究了间接直流电位法(IDC法)和交流电位法(AC法)用于监测疲劳短裂纹扩展速率的有关技术问题。
The technique of measurement of growth, rate of fatigue short crack with indirect KC (IDC) potential system and AC potential system was investigated.
本文采用断裂力学方法来估算结构构件的疲劳寿命,这其中主要围绕裂纹扩展速率表达式展开研究。
Fracture mechanics is adopted to estimate the fatigue life of structural members, and among the rest, crack growth rate formula is studied.