根据断口的宏、微观形貌,认为油管焊接后未及时消除焊接应力,产生了淬硬裂纹;
The macro and micro analysis of fracture indicates that it produces fracture because it doesn′t avoid welding stress in time.
某设备制造厂电机配水环管立缝在消除应力热处理后,熔合线附近出现裂纹。
A crack is found after SR heat treatment in the vertical welding fusion line for water distribution ring pipe of a electric machinery.
另一方面,热处理工艺不当使得铸造应力及机加工的残余应力无法彻底消除,这样加剧了裂纹的产生和扩展。
On the other hand, the improper heat treatment operation can not completely relieve the casting stress and remnant stress, and further enhances generation and expansion of cracks.