结果表明，短纤维的加入显著提高了SFRC的撕裂强度、10%定伸应力及邵尔A型硬度；
The results showed that the filling of short fiber evidently improved tear strength, modulus at 10%and Shore A hardness of SFRC.
详细研究了尼龙和聚酯短纤维用量对尼龙-天然橡胶和聚酯-氯丁橡胶复合材料的20％定伸应力、拉伸强度及撕裂性能的影响。
The influence of the loading level of nylon and PET short fibres was studied on the physical properties of Nylon-NR and PET-CR Composites, such as 20% modulus, tensile strength and tear resistance.
实验结果表明，振动力场的作用可以提高TPE的拉伸强度、100%定伸应力和扯断伸长，改善TPE的硬度。
The experimental results show that, under vibration force field, tensile strength, tensile stress at 100% and elongation at break of TPE can be enhanced, and hardness(shore A) of TPE can be improved.
例如，300%定伸应力提高了77%，抗撕裂强度提高了38%。
For instance, 300%modulus was increased by 77% and tear strength by 38%.
测试结果表明，随着蒙脱土用量的增加，复合材料的定伸应力、拉伸强度和撕裂强度均大幅度提高。
The results showed that the tensile strength, elongation at break and tear strength increased with the OMMT content increasing.
结果表明，高羧基丁腈橡胶具有硬度、拉伸强度和定伸应力高，耐磨性好，压缩永久变形大，加工安全性较差等特点；
The results showed that the high carboxylated NBR featured high hardness, tensile strength and modulus, good abrasion resistance, but greater permanent set and poorer processing safety;
结果表明，NBR/PVC共混硫化胶具有突出的耐油、耐臭氧老化性能，拉伸强度、定伸强渡和撕裂强度也较NBR有所提高。
The results showed that NBR/PVC blends exhibited good oil-resistance, ozone-resistance, and their breaking strength and tear-resistance strength were also rather improved.
结果表明，NBR/PVC共混硫化胶具有突出的耐油、耐臭氧老化性能，拉伸强度、定伸强渡和撕裂强度也较NBR有所提高。
The results showed that NBR/PVC blends exhibited good oil-resistance, ozone-resistance, and their breaking strength and tear-resistance strength were also rather improved.