结果表明，短纤维的加入显著提高了SFRC的撕裂强度、10%定伸应力及邵尔A型硬度；
The results showed that the filling of short fiber evidently improved tear strength, modulus at 10%and Shore A hardness of SFRC.
详细研究了尼龙和聚酯短纤维用量对尼龙-天然橡胶和聚酯-氯丁橡胶复合材料的20％定伸应力、拉伸强度及撕裂性能的影响。
The influence of the loading level of nylon and PET short fibres was studied on the physical properties of Nylon-NR and PET-CR Composites, such as 20% modulus, tensile strength and tear resistance.
实验结果表明，振动力场的作用可以提高TPE的拉伸强度、100%定伸应力和扯断伸长，改善TPE的硬度。
The experimental results show that, under vibration force field, tensile strength, tensile stress at 100% and elongation at break of TPE can be enhanced, and hardness(shore A) of TPE can be improved.
测试结果表明，随着蒙脱土用量的增加，复合材料的定伸应力、拉伸强度和撕裂强度均大幅度提高。
The results showed that the tensile strength, elongation at break and tear strength increased with the OMMT content increasing.
结果表明，高羧基丁腈橡胶具有硬度、拉伸强度和定伸应力高，耐磨性好，压缩永久变形大，加工安全性较差等特点；
The results showed that the high carboxylated NBR featured high hardness, tensile strength and modulus, good abrasion resistance, but greater permanent set and poorer processing safety;
结果表明，NBR/PVC共混硫化胶具有突出的耐油、耐臭氧老化性能，拉伸强度、定伸强渡和撕裂强度也较NBR有所提高。
The results showed that NBR/PVC blends exhibited good oil-resistance, ozone-resistance, and their breaking strength and tear-resistance strength were also rather improved.
结果表明，NBR/PVC共混硫化胶具有突出的耐油、耐臭氧老化性能，拉伸强度、定伸强渡和撕裂强度也较NBR有所提高。
The results showed that NBR/PVC blends exhibited good oil-resistance, ozone-resistance, and their breaking strength and tear-resistance strength were also rather improved.