The tensile strength and elongation after fracture vary little after rolling.
在下屈服强度降低的同时，其抗拉强度和断后伸长率变化不大。
After rolling, these inclusions turn from ball-like shape to chain-like and dot-linked shapes.
夹杂形状经轧制后由球形逐渐变为长条形和点链状。
The boundary condition of seaming and repairing of slabs interior defects after rolling were given.
给出了铸坯内部轧制时焊合及修复的边界条件。
According to the above mathematical model, it can calculate final ferrite grain size after rolling cooling.
按照上述给出的数学模型，可计算出轧制冷却后最终的铁素体晶粒的大小。
The steel is processed into standard samples for mechanical properties testing after rolling and heat treatment.
冶炼出的钢锭经过轧制，并进行热处理，加工成力学性能标准试样。
The replacement of tempering after rolling with TMCP for bainite transformation in SBL steel is a kind of diffusion type.
结果表明，控轧控冷代替常规轧后回火工艺的途径是可行的，并有力地支持了粒状贝氏体的扩散型长大学说。
In rolling mill, it is very important step which impact product quality that measure the thickness of mental after rolling.
在轧机行业中，金属板轧制后的厚度检测是影响产品质量的重要环节。
The results showed that after rolling at high and low temperature, skin-core structures also existed in the PP/LCP composite.
结果发现，PP/LCP复合材料经过高温、室温压延后仍存在皮芯结构；
After rolling, the player can choose to try for a bigger payout by rolling again, or stop and take all the ducats in the Pot.
掷骰结束后，玩家可以选择偿试更大的赌注在次掷骰，或停下来拿走赢得的所有钱币。
The British Standard grade 460 bars, which when quenched with left heat after rolling, are naturally aged for different times.
对采用轧后余热处理工艺生产的英标460级钢筋进行不同时间的自然时效后测定其力学性能。
Seen here after rolling back before Thursday's shuttle launch, the RSS provides pre-launch access to the orbiter and its payload.
这里可以看到在星期四傍晚，太空梭发射前，RSS 与太空梭及其负载接近的情形。
New TMCP, which hot ribbed bar is produced with ultra fast cooling technology after rolling, is a creative, applicable technology.
新一代TMCP -轧后超快速冷却技术生产热轧带肋钢筋是一种创新性的适用技术。
The morphology of sulphide inclusions in sulphur-comprising microalloyed steel manufactured by converter after rolling was observed.
用金相显微镜、扫描电镜和能谱观察和分析了转炉生产的含硫非调质钢轧后硫化物夹杂的形貌。
The morphology of sulphide inclusions in sulphur-comprising micro alloyed steel manufactured by converter after rolling was observed.
用金相显微镜、扫描电镜和能谱观察和分析了转炉生产的含硫非调质钢轧后硫化物夹杂的形貌。
The morphology of sulphide inclusions in sulphur-comprising micro alloyed steel manufactured by converter after rolling was observed.
本文研究了转炉生产含硫非调质钢中硫化物夹杂的控制方法。
The carbon content of the tundish is different from the steel coil after rolling, the carbon content of the steel coil is significantly lower.
中间包的碳含量与轧制后钢卷的碳含量不同，轧制后钢卷的碳含量明显要低。
This paper intends to study the influence of rapid cooling time after rolling on the microstructure and mechanical properties of low-carbon steel.
本文研究了轧后快冷时间对控轧低碳钢板组织和力学性能的影响。
Various alclad, heating time, rolling pass, reduction is used in the test, and compared surface quality with rate of finished product after rolling.
本试验采用不同包铝方式，不同加热时间，不同轧制道次和道次压下量的安排进行研究。
From out of billet steel plant also is only semi-finished products, to the rolling mill to be carried out after rolling to become qualified products.
从炼钢厂出来的钢坯还仅仅是半成品，必须到轧钢厂去进行轧制以后，才能成为合格的产品。
The fast heating method could be used in the rolling process for the material which was required to keep its original structure and property after rolling.
利用快速加热还可对轧后需保持原有组织和特性的材料进行轧制。
The result shows that the inclusion, high cooling speed and uneven of cooling speed after rolling are the main reasons for steel plate cold bending rupture.
结果表明，钢板中有较多的非金属夹杂物及轧后冷却速度过快和冷速不均匀是导致冷弯性能不合格的主要原因。
And also the control function of the equipments at the slab yard before rolling and at the finishing line after rolling are held in the hands of the computers.
对轧制线的前工序板坯堆放场和轧制线的后工序精整线也同样由微型机分别承担每台设备的控制功能。
After rolling, the tea was sent back to the drying pans for a second round of firing, losing even more volume at every contact with the hot sides of the iron wok.
揉捻之后，茶叶被运回炒锅里开始第二轮翻炒，那些紧贴着炙热铁锅的茶叶的体积将进一步缩小。
Other bars and rods of iron or non-alloy steel, not further worked than forged, hot-rolled, hot-drawn or hot-extruded, but including those twisted after rolling.
铁或非合金钢的其他条、杆，除锻造、热轧、热拉拔或热挤压外未经进一步加工，包括轧制后扭曲的。
Compared with the thread obtained by cutting process, the shear strain and hardness of 304 steel pipe thread has been increased significantly after rolling process.
与套丝加工相比，滚压加工后304钢管螺纹的抗剪拉力和硬度均有大幅提高。
As to the flatness calculating of CVC mill, a software is developed to predict the strip thickness distribution after rolling by using the influence function method.
针对C VC热连轧精轧机组板形计算问题，采用影响函数法开发了计算热连轧机轧后板断面厚度分布的软件。
The results show that the decarbonization of Si Mn bearing spring steel mainly occurs both in the heating process prior to rolling and in the cooling process after rolling.
结果表明：硅锰弹钢脱碳主要发生在轧前加热过程中，轧后冷却也发生脱碳。
The results show that the decarbonization of Si Mn bearing spring steel mainly occurs both in the heating process prior to rolling and in the cooling process after rolling.
结果表明：硅锰弹钢脱碳主要发生在轧前加热过程中，轧后冷却也发生脱碳。