高压铝阳极氧化膜的陷阱浓度与隧穿导电。
The trap concentration and tunnel conductance in aluminum anode oxidized films under high field.
对影响氧化膜封闭质量的主要因素进行试验。
The major factors which influence sealing quality of aluminium oxides are investigated.
素材氧化严重,如氧化斑,热处理后氧化膜。
Material oxidation, such as oxidation spot, serious after heat treatment of oxide film.
通过试验,研究了常温封孔氧化膜的陈化特性;
The ageing characteristics of sealed oxide film at normal temperature are studied.
较高的峰值电流密度导致氧化膜的外边缘破裂;
Higher peak current densities resulted in the cracking of the outside edge of the pores.
讨论了合金表面粗糙度对氧化膜开裂行为的影响。
The effect of alloy surface roughness on the oxide cracking behavior was discussed.
钛植入体的生物学性能取决于其表面氧化膜的表征。
The Biological properties of titanium implant depend on its surface oxide film.
目的:研究阳极氧化对纯钛种植材料氧化膜的影响。
Objectives: To study the oxide film of pure titanium implant material treated by anodic oxidation .
化学氧化:通过化学处理使金属表面形成氧化膜的过程。
Chemical oxidation: through the chemical processing the metal surface oxidation film formation process.
与此同时,应力和活性阴离子对氧化膜的破坏造成孔蚀;
At the same time, stress and active anion will destroy the oxidic film.
本文研究了一种铝合金阳极氧化膜新型的绿色封闭工艺。
A new green sealing process of anodic oxide film of aluminum alloy was studied in this paper.
采用SEM对试样表面生成氧化膜的形貌进行了观察比较。
The morphology of oxide membrane on each sample surface was observed by SEM.
这表明,问题可能在于薄氧化膜形成的接触和分解时,感动。
This indicates that the problem probably lies in a thin oxide film that forms on contacts and breaks down whenever moved.
低温下进行水热处理,羟基磷灰石晶体在氧化膜的表面沉积。
Hydroxyapatite crystals were precipitated on film surfaces at low temperature hydrothermal treatment.
必须先做除锈及去氧化膜处理,一般使用化学抛光或电解抛光。
Must do derusting and to oxidation film processing, generally use chemical polishing or electrolytic polishing.
探讨了铝合金多孔氧化膜的热封闭机理,优选了热封闭添加剂。
The mechanism of the hot sealing of anodic film of aluminium alloy is discussed.
潮湿的盐雾环境和化学氧化膜的薄而软是引起腐蚀的主要原因。
It is mainly reason that wet and salt spray environment and thin film of chemical oxidation.
铜管脱脂,氮气保护退火对降低氧化膜中碳的含量无明显效果。
The intermedium pickling and oxidation annealing can greatly reduce the carbon content in the oxide film.
结果表明,通过硫酸钇脉冲封闭,可以将钇元素引入到氧化膜中。
The results indicated yttrium was introduced into the anodic film by yttrium salt sealing.
利用XRD和SEM分别对氧化膜的相组成和表面形貌进行了分析。
XRD and SEM were employed to characterize the phase component and surface morphology of the films.
讨论了氧化溶液组成和操作条件对氧化膜耐蚀性和接触电阻的影响。
Influences of solution component concentrations and working conditions on corrosion resistance and contact resistance of the film obtained are discussed.
目的:了解电解质和电压因素对氧化膜成分、形态和稳定性能的影响。
Objective: To know the effects of electrolyte and voltage on the property of anodic oxide films.
非欧姆接触可能发生在由氧化膜形成的低压电路或其它非线性连接中。
Nonohmic contacts may occur in a low voltage circuit as a result of oxide films or other non-linear connections.
当占空比为10%时,得到最大的氧化膜厚度和最佳的氧化膜截面形貌。
The oxide film formed at the duty cycle of 10% has a maximum thickness and best section morphology.
结果表明:钛氧化膜的溶解和膜中存在离子缺陷有关,膜溶解遵从对数规律。
The results indicate depentence of the film dissolution pn the ionic defect. The, film dissolution obeys the logarithm law.
为了研究阳极氧化工艺条件对硬质氧化膜的厚度、耐蚀性、表面形貌的影响。
The effects of anodic oxidation process on thickness, corrosion resistance and surface morphology of hard oxidation film were studied.
结果表明稀土封孔阳极氧化膜的耐蚀性与铬酸盐封闭阳极氧化膜具有可比性。
The results show that rare earth sealing for anodized film is comparable to that of chromate sealing.
阳极沉积阶段是在阳极表面形成团絮状的沉积氧化膜及氧化膜不断扩展的过程;
In the first stage of anodic deposition, the flocculent oxidation film deposits and extends on the surface of magnesium alloy.
通过扫描电镜和电子探针发现,LY12型铝合金棱角部位阳极氧化膜产生了裂纹。
SEM and EPM results indicate that cracks form at edges and corners of LY12 aluminum alloy's oxide film.
通过扫描电镜和电子探针发现,LY12型铝合金棱角部位阳极氧化膜产生了裂纹。
SEM and EPM results indicate that cracks form at edges and corners of LY12 aluminum alloy's oxide film.