By substituting calcium carbide sludge for limestone, raw material had fairly good burnability and cement clinker had high quality.
利用电石渣取代石灰石后生料具有较好的易烧性,可以烧制优质水泥熟料。
参考来源 - 利用电石渣生产水泥的研究Reuse of water purification sludge as silica material, with modulus (KH=0.91, IM=1.30, SM=2.37), the effect of the sludge on clinker sintering and properties of the clinker were studied.
1.利用杭州水业集团排放的污泥配料烧制水泥,KH=0.91,IM=1.30,SM=2.37,研究不同掺量对生料易烧性和熟料性能的影响。
参考来源 - 污泥替代硅质原料烧制水泥Increasing the content of C3S in cement is a best way of gaining high strength cement, but means the higher burning temperature.
提高C_3S含量,是获得高胶凝性硅酸盐水泥的有效途径,但熟料的烧成将同时变得困难,也即存在易烧性与胶凝性的矛盾,因此,要获得高C_3S熟料,提高相应的高钙生料的易烧性是关键。
参考来源 - 高钙生料易烧性初步研究·2,447,543篇论文数据,部分数据来源于NoteExpress
与石灰石相比,硅质原料性质对生料易烧性影响更大。
Compared with that of limestone, the properties of siliceous material will have more influence on the burnability of raw meal.
本文研究了以黄沙或页岩代替粘土质原料配制水泥生料的易烧性。
The burnability of the cement raw meal prepared by shale or yellow-sand has been studied in this paper.
同时,电石渣有利于改善生料易烧性,降低熟料热耗,节约能源。
Besides, calcium carbide slag is favorable to improve burn-ability of raw meal, and to reduce heat consumption of clinker for energy saving.