在不同的微蚀温度、时间条件下,研究了高锰酸钾微蚀溶液对环氧树脂层压板和3240型环氧树脂板(基板)微蚀作用的影响。
Effect of potassium permanganate etching solution on the roughening of epoxy resin laminates board and 3240 epoxy resin board at various temperatures and times was investigated.
同时对影响产率的因素:高锰酸钾和水用量,反应时间、反应温度等作了探讨。
The factors which affected the rate of product, such as capacity of potassium permanganate and water, time and temperature of the reaction were inquired into.
当高锰酸钾浓度为4%、加入量为3%、氧化时间为20分钟时.所制得改性淀粉粘合剂的各项性能均较好。
When content of KMnO4 4 % , adding amount 3 % , oxide time 20 mm, the properties of modified starch adhesive were super.