经x射线衍射分析,纯钛表面经阳极氧化处理后,其表面生成了一层非晶态的氧化钛薄膜,并且钛晶体的各个表面沿不同结晶方向的腐蚀速率不相同。
XRD results indicate that amorphous titanium oxide film is formed on the surface after anodic oxidation, and corrosion rates of titanium crystal vary along different crystalline orientation.
微弧氧化陶瓷层的耐蚀性优于阳极氧化和铬化处理膜层的耐蚀性。
The corrosion resistance of micro arc oxidation ceramic coating is better than the corrosion resistance of chromate and anode coating.
将超声波应用于铝的阳极氧化处理,研究了超声波对阳极氧化特性曲线、 电解工艺参数和膜层形貌的影响。
The ultrasonic technics was applied to anode oxidation of aluminum. The influences of ultrasonic on anode oxidation curves, electrolytic process parameters and oxide film's morphology were studied.