... 净收入 net revenue 造孔剂 foam-introducing agent 造孔剂 pore forming additive ...
基于6个网页-相关网页
... foreign investment law of china 韩国外资法 pore forming additive 造孔剂 representative structure 典型结构件 ...
基于6个网页-相关网页
The appearance of macropore formed by urea volatilization was similar to urea, and the porosity could reach 85% by adding pore-forming agent.
添加造孔剂尿素生成的大孔形貌与造孔剂基本一致,孔隙率可达85%。
参考来源 - 多孔NiAl金属间化合物/陶瓷复合材料的研究Microporous hydroxyapatite crystal has been synthesized using calcium nitrate and phosphorus oxide by hydrothermal method without any pore-forming material and template.
在没有加入任何造孔剂或模板剂的条件下,在碱性介质中通过水热合成制备了晶体发育完整,晶体表面孔洞分布均匀的六方柱状纳米羟基磷灰石晶体。
参考来源 - 纳米羟基磷灰石及HAP/PMMAPore former affects pore structure and strength of the products. Charcoal powder can make the products with the best general properties, so it is the optimum one among the four discussed pore former materials.
造孔剂影响制品的孔隙结构和强度,在所实验的四种造孔剂原料中,炭粉作为造孔剂所得制品的综合性能最好,是理想的造孔剂;增加造孔剂用量,使孔隙结构由单孔向网状连通孔转变。
参考来源 - 矿物多孔材料的制备及其性能研究The spherical-like pores with the diameters of 100~600μm distributed uniformly in the bond when using marble as pore former.
结合剂中的气孔率及孔径与烧成温度、造孔剂粒度及其质量百分数有关。
参考来源 - 硼硅玻璃系陶瓷结合剂的强度优化与气孔调控The effects of amount of pore-forming material and bonding, and sintering temperature on the porosity and flexural strength of porous alumina ceramic were analyzed by orthogonal experiment.
通过正交试验分析了造孔剂添加量、粘结剂添加量和烧结温度对多孔氧化铝陶瓷气孔率和弯曲强度的影响。
参考来源 - 多孔氧化铝陶瓷的制备及性能研究Firstly, the influence of pore-former in anode substrate on single cell was investigated.
首先考察阳极中造孔剂的含量对单电池的影响。
参考来源 - YSZ电解质薄膜丝网印刷制备工艺的阳极参数研究·2,447,543篇论文数据,部分数据来源于NoteExpress
随着造孔剂含量的增加,预制体气孔率升高。
The porosity of preforms increased with the increase of starch contents.
实验研究分析了添加炭粉造孔剂和改进喷涂工艺参数对阳极层孔隙率的影响。
The influence of added charcoal pore-forming agent and improved plasma spraying parameters on porosity of the anode layer were investigated experimentally.
本文介绍了在UO_2粉末中加入造孔剂制备低密度uo_2燃枓芯块的方法。
In this paper, the method fabricating the lower density UO_2 fuel pellet is investigated.