结果表明,82 B钢盘条脆断的主要原因是夹杂物级别超标、组织中出现网状碳化物、索氏体含量偏低以及盘条表面缺陷等。
The results show that 82b wire rod brittle fracture is mainly caused by excessive inclusion, reticulate carbide, lower sorbite in the microstructure, and surface defect of wire rod.
热处理、碳化、淬火硬化层,表面覆层,钢,有色金属,微小及薄形零件等。
Heat treated layer, carbonized layer, hardened hard layers, superficial coating, steels, non-ferrous metal, micro and thin shaped components.
利用纯镍标识钢的原始表面,研究了钢经td处理所产生的碳化钒覆层形成过程。
The original surface of a steel specimen was identified by pure nickel so as to study the formation process of a vanadium carbide coating on the surface of the steel specimen through TD treatment.