对于缺口疲劳试样,则采用半寿命阶段的疲劳参数的预测结果为最小。
As for notched specimen, the fatigue life prediction using fatigue factors of half-life section is the smallest.
测定了300M钢的缺口疲劳始裂寿命曲线,给出了估算疲劳始裂寿命的方法。
The fatigue crack initiation life of 300M steel is experimentally investigated and a simple method for predicting the fatigue crack initiation life of materia is offered.
预过载拉伸可提高铝合金缺口疲劳寿命,但效果不及喷丸; 过载量太大还使寿寿命趋于子下降。
The experiments on notched specimens of an Aluminium alloy indicat that the notch fatigue life can be increased by a tensile over-pre loading but decreased by a compressive over-pre loading.