The measuring of the content of holo cellulose in fibremateria ls follows the nationa l standard 2677.10-1995, the measuring of the content of ligninfollows the nationa l standard 2677.8-1994.
测量植物纤维原料中综纤维素含量的方法主要是依据国标GB/T 2677.10-1995，测量木质素含量的方法主要是依据国标GB/T 2677.8-1994。
参考来源 - 化学计量学和近红外光谱法用于木材与竹材品质研究The results as follows:1. The amount of holocellulose, lignin, density, and microfibril angle of Chinese fir were predicted by using back-propagation neural network (BP-ANN) combined with near infrared (NIR) spectrometry.
本文研究内容包括以下四个方面:1.利用近红外光谱(NIR)技术结合反向传递神经网络法(BPNN)定量预测了杉木中的综纤维素、木质素、密度和微纤丝角。
参考来源 - 化学计量学与近红外光谱法在木材与奶粉品质分析中的应用·2,447,543篇论文数据，部分数据来源于NoteExpress
综纤维素的近红外预测值与木粉颗粒度之间不存在统一的规律性。
The predicted value of holocellulose has nothing to do with the change of size of example.
结果表明：微生物酶使木粉的玻璃化温度降低，纤维素的结晶度提高，综纤维素含量以及纤维素聚合度降低；
The result indicates:handled by enzyme, the wood's glass transition temperature, holo-cellulose content and degree of polymerization increased, crystallinity increased;
将毛头鬼伞菌丝体接种到不同栽培培养基上，分析了菌丝体对培养基中综纤维素、木质素以及淀粉利用的动态变化。
This experiment investigated the relationship between mycelial growth of Coprinus comatus and utilization of holocellulose, lignin and starch in culture materials.
综纤维素，又称总纤维素（total cellulose），是指造纸植物纤维原料除去抽出物和木质素后所留下的部分（即半纤维素和纤维素的总称），其制备方法有： （1）氯化法：此法为1937年由里特（Ritter）等提出，用氯气处理无抽提物的木粉，然后用乙醇胺的乙醇溶液抽提，将氯化木素溶出，残渣即为综纤维素。 （2）亚氯酸钠法：1942年杰姆（Jayme）等提出用亚氯酸钠处理无抽提物的木粉，将木素氧化、除去，得到含有部分降解的碳水化合物的产物即为综纤维素。 （3）二氧化氯法：1921年斯密特（Schmidt）等建议用二氧化氯加碳酸氢钠的饱和溶液处理无抽提物木粉，把其中的木素氧化而除去，残渣即为综纤维素。 （4）过醋酸法：在醋酸钠溶液中加入醋酸酐和过氧化氢形成过醋酸溶液，用它在70℃下处理无抽提物试样，将其中的木素氧化而除去，残渣即为综纤维素。 应该指出，所得到的综纤维素中仍含有少量的木素，而且在制备过程中往往会有少量的碳水化合物被溶出。