与经普通淬火和高温回火的相比，经磁场淬火和高温回火的T10钢的抗拉强度提高了28%，断后伸长率提高了8。
The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
经焊后回火热处理后，主要合金元素沿焊合区的扩散区宽度增大；焊合区钛合金侧硬度值显著提高。
The diffusion zone width of main alloying elements increases and hardness of the friction weld zone near TC4 titanium alloy side improves after post-weld heat treatment.
经淬火及回火后的合金层具有高速钢组织及性能。对渗金属层渗碳后的组织进行了电子显微分析。
The carburized alloyed layer possesses high density of finery and dispersed alloy carbides for the high concentrations of W, Mo and their affinities with carbon.