疲劳试样多数断于接头的热影响区,造成这一结果的主要原因是热影响区的组织不均匀性和氢含量相对较高。
The fracture occurres at heat affected zone (HAZ) of most fatigue specimens. This is due to the structure inhomogeneity and the higher hydrogen content of materials at HAZ.
结果表明:回火索氏体是最佳的组织形态;微观硬度的不均匀性显著影响钢的表面加工质量。
The results indicated that the tempered sorbite was the optimum microstructure, the inhomogeneous distribution of micro hardness affected markedly the finish quality of the steel surface.
本文采用概率断裂力学方法和可靠性分析方法,针对压力容器焊接接头的组织不均匀特点,研究了焊缝区疲劳失效概率模型。
The paper studies the fatigue failure probabilistic model of the weld zone in welded joint using probabilistic fracture mechanics and reliabilitistic analysis methods.