结果表明,随轧制道次的增加,晶粒尺寸逐渐减小,索氏体的含量不断增加,屈服强度逐渐提高。
The results indicate that, with the increase of rolling times, the grain size becomes smaller, the content of sorbite multiplicates, and the yield strength improves.
结果表明,82 B钢盘条脆断的主要原因是夹杂物级别超标、组织中出现网状碳化物、索氏体含量偏低以及盘条表面缺陷等。
The results show that 82b wire rod brittle fracture is mainly caused by excessive inclusion, reticulate carbide, lower sorbite in the microstructure, and surface defect of wire rod.
结果表明:回火索氏体是最佳的组织形态;微观硬度的不均匀性显著影响钢的表面加工质量。
The results indicated that the tempered sorbite was the optimum microstructure, the inhomogeneous distribution of micro hardness affected markedly the finish quality of the steel surface.