穿晶裂纹源于晶内形变损伤区,其扩展机制为沿滑移面的剪切断裂。
Tranagranular cracks result from deformation damage of grain, and its propagation mechanism is shear rupture along slip plane.
裂纹形成的断裂为穿晶解理机制,预应变可导致更多的二次裂纹。
The fractography of the fatigue crack initiation displayed cleavage facet and more second cracks after pre-training.
研究表明该钢具有较好的抗应力腐蚀性能,其应力腐蚀断裂形貌为穿晶、解理断裂,并有二次裂纹。
The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.