结果表明,黄铜管的开裂为氯离子引起的穿晶应力腐蚀开裂;
The results showed that it was chlorine ion that resulted in transgranular stress corrosion cracking in brass tubes.
研究表明该钢具有较好的抗应力腐蚀性能,其应力腐蚀断裂形貌为穿晶、解理断裂,并有二次裂纹。
The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
钠腐蚀后,两种钨试样的沿晶脆断特征变得更为显著,为沿晶和穿晶混合型脆性断裂。
The brittle morphologies become much more notable, and appear the inter-and trans-granular fracture mode after sodium corrosion at high temperature for both of W-specimens.