介绍了冶金起重机金属结构偏轨箱形模拟主梁的疲劳失效分析研究结果,提出疲劳失效的原因及改进措施。
Failure analysis of side rail box imitating chief beam of metallurgy crane was studied. Cause of fatigue failure and improving method were given.
对某车型发动机排气歧管的热疲劳断裂问题进行综合失效分析,并从材料、结构方面提出改进意见。
This paper gives a comprehensive failure analysis on the thermal fatigue crack of engine exhaust manifold and makes an improvement for materials and structures.
以实测为根据,应用断裂理论对滑块式联接轴叉头进行了失效分析,并提出了提高疲劳寿命的措施。
The failure analysis for universal shaft joint based on measuring results as well as fracture mechanic is carried out. And proposals of improving its endurance life are suggested.