研究结果表明,前叉立管在周期应力作用的环境中使用,非常容易形成疲劳裂纹,由此导致了摩托车前叉立管的断裂现象。
The investigation shows that the vertical shaft of the front fork is subject to fatigue flaw due to the cyclic stress, which leads to the fracture of the vertical shaft.
环境辅助裂纹是已知的材料,可以受环境和应力的影响。
The environmental assisted cracking is known as the cracking in material that can be affected by the environment and the stress.
由此确定了不同材料在不同环境溶液中的临界裂纹尺寸,得到了气瓶工作压力及等效应力与临界裂纹尺寸的关系曲线。
The critical crack sizes of different materials in H_2S environment were thus figured out, and the curves with working pressures and equivalent stress to critical crack size were plotted.