通过综合分析指出对流管发生失效的原因是奥氏体不锈钢长期在高温下工作引起的热脆化开裂。
Through the comprehensive analysis, the result shows that crack failure reason is embrittlement of the austenite stainless steel at high temperature.
在试验的焊接条件下,WCX355超细晶钢在热影响粗晶区未有明显脆化,在回火区也未发生软化现象。
Under the experiment's welding condition, WCX355 ultrafine grained steels didn't distinctly embrittle in CGHAZ and didn't soften in tempering zone either.
粒状贝氏体及粒状组织中的M-A岛不是该钢焊接热影响区过热区脆化的原因。
The M-A units in granular bainite and granular structure are not the cause of embrittlement.