用该合金作为触媒合成金刚石可提高其强度,并随渗氮层厚度的增加强度也增加。
When the a1loy is used to synthesize the diamond, strength of the diamond is increased, and the thicker the nitriding case, the higher the strength.
液体渗氮可以获得厚度为0.001到0.012英寸(0.03~0.30mm)的硬化层,然而气体渗氮则能获得厚0.025英寸(0.64mm)的硬化层。
Case thickness of 0.001 to 0.012in. (0.03~0.30mm) is obtained, whereas for gas nitriding the case may be as thick as 0.025 in. (0.64mm).
以获得较高表面硬度和渗层厚度为依据,分析影响渗氮层结构和性能的主要工艺因素,确定出最佳工艺参数。
For obtaining high surface hardness and great thickness, the main factors which affect the nitriding layer structure and properties were analyzed, and the optimized parameters were obtained.