淬硬钢:一般都是高碳钢或者是高合金钢。 因其高碳、高合金性,再淬火后钢铁表面的硬度会大幅度提高而命名。
文章详细信息 关键词: 淬硬钢;;高速铣削加工;;有限元模拟 [gap=1136]Keywords: Quenched steel;High speed milling;Finite element simulation
基于700个网页-相关网页
... Chilled Hardened Steel 听听 良兴儿童早教机建筑铸钢淬火钢 Chilled Steel 淬火钢; 淬硬钢 Chisel Steel 凿钢; 凿子钢 ...
基于624个网页-相关网页
... hardening furnace淬火炉 hardening steel淬硬钢 hardening temperature淬火温度 ...
基于136个网页-相关网页
... Air quench hardening glass 风冷钢化玻璃 quench hardening steel 淬硬钢 ir quench hardening glass 风冷钢化玻璃 ...
基于98个网页-相关网页
自淬硬钢 Self-Hardening Steel ; Hardening Steel
空冷淬硬钢 Self-Hardening Steel ; Hardening Steel
全淬硬钢 Full-Hardened Steel
自淬硬钢钢轨 Rail Of Self-Hardening Steel ; Hardening Steel
空气淬硬钢 air hardening steel
水淬硬钢 water hardening steel
淬硬钢衬套 hardened steel bushing
淬硬钢板 hardened plate
淬硬钢和回火钢 Steels for quenching and tempering
It is an advantage of high speed processing that cutting hardened steel directly by coated tool. This reduces the product processing step directly, shortens the product processing time.
用涂层刀具直接加工淬硬钢是高速加工的优势,这直接减少了产品的加工步骤,缩短了产品的加工时间。
参考来源 - 高速铣削切削力变化及刀具轨迹优化研究·2,447,543篇论文数据,部分数据来源于NoteExpress
磨削热导致回火引起淬硬钢磨削后表面硬度变化。
Tempering resulting from grinding heat caused surface hardness changes of hardened steels after grinding.
回火完全淬硬钢得到的最终组织结构被称为回火马氏体。
The final structure obtained from tempering a fully hardened steel is called tempered martensite.
由于马氏体这一淬硬钢主要成分的不稳定性,使得回火成为可能。
Tempering is possible because of the instability of the martensite, the principal constituent of hardened steel.