次层为淬火马氏体组织;
原始材料的组织状态为形变马氏体、淬火马氏体及残余奥氏体。
The original structure consists of deformation induced martensite, quenching martensite and retained austenite.
结果表明:由于焊接电流过大,使焊缝产生淬火马氏体组织及较大的焊接残余应力,导致镀锌氢脆敏感性增加,造成吸油盘发生氢脆开裂。
The large welding current caused the formation of quenched martensite and the high residual stresses in the welding zone, resulting in the increase of zinc sensitivity of hydrogen attack.