The phosphate lubricant coating and oxalate lubricant coating were successfully gained during the surface preprocessing of TC4 titanium alloy,their thickness could be reached 2μm and 20μm,respectively.
TC4钛合金坯料拔前经过表面预处理过程,成功制得了磷酸盐润滑涂层及草酸盐润滑涂层,其厚度分别达2μm和20μm,各涂层与TC4合金基体结合致密,为润滑剂的附着提供了良好的载体,同时可以起到隔离坯料和模具直接接触的作用。
参考来源 - TC4钛合金棒线材冷拉拔加工工艺研究The lubricant coating was used in thin checking gloves.
将润滑涂层应用到薄型检查手套上,对传统乳胶手套的浸渍生产工序进行改进。
参考来源 - 检查手套润滑涂层的制备与机理研究·2,447,543篇论文数据,部分数据来源于NoteExpress
采用碳化铬、镍铬合金、氟化物共晶体和银的复合粉末为原料,通过等离子体喷涂方法制备高温耐磨自润滑涂层。
Self-lubricating wear resistant coating is prepared by plasma spraying using chromium carbide, nickel chrome, fluoride-metal, and silver composite materials.
本研究利用自制的纳米尺寸的硫化亚铁颗粒作为等离子喷涂的喂料,在钢基体表面制成了纳米硫化亚铁自润滑涂层。
In this paper, the nano iron sulfide plasma spraying feedstocks were made by oneself and the nano self-lubricating coatings on the steel were fabricated by plasma spraying.
综述了多种硫化物自润滑涂层的制作工艺,着重介绍了最新开发的纳米硫化亚铁热喷涂涂层的工艺、形貌、性能以及应用前景。
The new invention on nano-structured sulfide self-lubricating coatings produced by thermal spraying was specially introduced by showing their technology, appearance and capability.