Zinc immersion is conducted in a solution with immersion time for 1～2min at the operating temperature of 65℃.2.
浸锌温度为65℃,时间1～2min。
参考来源 - 镁合金表面电沉积镍的研究·2,447,543篇论文数据，部分数据来源于NoteExpress
对浸锌前处理的碱蚀和出光的改进方法进行了总结。
Improvement in alkaline etching and smut removing before zincate treatment was summed up.
在浸锌液的日常维护中，掌握浸锌液中锌的含量非常重要。
It 's very important to know zinc content in zinc dipping solution during its everyday maintenance.
二次浸锌得到的锌晶粒比一次浸锌更细小、均匀和致密，对基体覆盖能力好。
Finer, more uniform and denser zinc crystals were attained by secondary zinc coating with better covering capacity.