文章详细信息 关键词： TRIP钢;;残余奥氏体;;锰;;退火;;微观组织 [gap=839]Keywords: TRIP steels;retained austenite;manganese;annealing;microstructure
基于164个网页-相关网页
深冷处理对轴承稳定性影响的研究 关键词】：轴承钢；深冷处理；残余奥氏体 [gap=585]Keywords】：bearingsteel；cryogenictreatment；austeniteresiduum
基于18个网页-相关网页
高铬铸铁残余奥氏体测定的探讨-机械资料KV99.COM 关键词： 高铬铸铁：x射线衍射；磁性法；残余奥氏体 [gap=426]key words: high chromium cast iron, x-ray diffraction, magnetic
基于12个网页-相关网页
The experimental result indicates that the volume fraction of cementite and transition carbides (unstable) precipitated in martensite matrix increase, while the volume fraction of the retained austenite decreases with increasing partitioning time.
实验表明随碳分配时间的增加,碳化物析出增多,残余奥氏体含量减少。
参考来源 - 高强度Q&P钢和QLaser melted zone is composed of cellular structure and dendritic crystals, and the microstructures are martensite, residual austenite and disperse carbide, also HAZ is mainly composed of martensite, residual austenite and carbide.
熔凝区主要由胞状晶+树枝晶组成,显微组织为马氏体、残余奥氏体和弥散分布的碳化物,热影响区主要由马氏体、残余奥氏体和碳化物组成。
参考来源 - 合金钢轧辊激光快速熔凝组织及性能研究·2,447,543篇论文数据，部分数据来源于NoteExpress
对高铬铸铁残余奥氏体测定的几种方法进行了比较。
Some methods of retained austenite measurement on high chromium cast iron were compared.
减少残余奥氏体和马氏体碳化物的降水预计的回火工艺。
Retained austenite reduction and carbide precipitations in the martensite are anticipated by the tempering process.
研究用钢的室温组织为贝氏体、马氏体、少量残余奥氏体。
The structure of the studied steels was bainite, martensite and retained austenite.
奥氏体是铁的一种相，另一种常见相是马氏体，过冷奥氏体是指在一定过冷度下未发生马氏体转变的奥氏体，残余奥氏体是指发生马氏体转变后，还有一定量未发生转变的奥氏体。 钢在淬火后总会保留一部分未转变的奥氏体称为残余奥氏体。不同的钢种残余奥氏体量也不一样。对碳钢来讲在含碳量大于0.4%的条件下，在显微组织中可以观察到残余奥氏体，含碳量越高残余奥氏体的数量越多。在相同含碳量的条件下，合金钢比碳钢的残余奥氏体量多，对一些高碳高合金钢，残余奥氏体量可以达到30～40%以上。残余奥氏体的存在使钢的性能变坏，如使弹性极限下降，零件的尺寸不稳定等。因此有必要了解残余奥氏体在回火过程中所发生的转变，以便设法控制之。