干滑动磨损性能 dry sliding property
High-temperature dry sliding wear behavior of coating was focused on. Studies have shown that temperature has a great influence on wearing resistance.
本文重点研究了喷焊层的高温干滑动磨损行为。
参考来源 - 新型热剪刀片表面喷焊复合材料的研究与应用·2,447,543篇论文数据,部分数据来源于NoteExpress
高钒高速钢干滑动磨损机理为显微切削和疲劳磨损的复合,并且有应力作用下碳化物的碎裂及脱落。
The wear mechanism of high vanadium high-speed steel is combined micro-cutting and fatigue wear with carbide particle breaking and peeling off under stress.
在干滑动摩擦过程中,磨损机制主要为氧化磨损和粘着磨损。
The wear mechanisms during dry sliding process are oxidation wear and adhesive wear.
干滑动摩擦磨损率随磨损滑移距离的增加先增加而后逐渐降低,磨损机制主要为粘着磨损和氧化磨损。
The wear rate initially increases and then decreases with sliding distance increasing in all tested materials, wear mechanism during dry sliding process is oxidation wear and adhesive wear.