Polyimide/barium titanate(BaTiO3) composite films have been fabricated using PMDA/ODA based polyimide as the matrix.
以PMDA/ODA基聚酰亚胺为聚合物基体,采用原位分散聚合法制备了聚酰亚胺/钛酸钡复合薄膜。
参考来源 - 功能性聚酰亚胺纳米复合薄膜的制备及性能研究Acidic environment, a five-storey composite membrane of pulling speed of 4.4 mm/s and 450℃for the calcination temperature were the most optimum conditions for the MWNTs/TiO_2 films.
酸性环境,提拉速度4.4mm/s时形成五层复合膜以及450℃的煅烧温度为MWNTs/TiO_2复合薄膜的最优化条件。
参考来源 - MWNTs/TiOThe optical absorption properties of Ag-BaO composite thin film with excess barium were measured while a vertical electric field was applied on the film surface.
对超额Ba激活的Ag-BaO复合薄膜在外加垂直表面电场作用下的光学吸收特性进行了测量。
参考来源 - Ag·2,447,543篇论文数据,部分数据来源于NoteExpress
结果表明:透明的银锌复合薄膜具有优良的抗菌性能。
It was found that silver zinc composite thin film was transparent and had an excellent antibacterial action.
采用溶胶-凝胶法在玻璃表面制备出透明的憎水性纳米复合薄膜。
Transparent nano composite film on the surface of glass of hydrophobic property is prepared with sol-gel processing.
利用光学吸收谱和Z -扫描技术研究了该复合薄膜的线性和三阶非线性光学性能。
Optical absorption spectroscopy and Z-scan technique were used to measure linear absorption and third-order optical nonlinearity of the films.