复合型裂纹起裂、扩展和止裂问题一直是断裂力学研究的重点。
The study of problems involving crack initiation, propagation and arrest is always the interest of fracture mechanics.
还会形成穿透型裂纹,造成镀层下本体金属的疲劳或应力腐蚀裂纹。
Through-thickness cracking also can lead to fatigue or stress corrosion cracking of the base metal beneath the plating.
利用当量直线裂纹扩展法研究复合型裂纹的能量释放率及相应的断裂判据。
The energy release rate and failure criterion for mixed mode are investigated by means of the method of equivalent linear crack extension.