• absorbency - 引用次数：14

  The key factors of influence on absorbency including the degree of neutralization, the amount of initiator and crosslinking agent as well as the amount of kaolin have been discussed.

  研究了单体中和度、高岭土加入量、交联剂用量、引发剂用量等影响吸水倍率的主要因素。

  参考来源 - 聚丙烯酸盐/高岭土高吸水性树脂的合成与性能研究
  hydrogel - 引用次数：5

  The swelling ratio of the hydrogel at absorption equilibrium depended on the sample weight, swelling ratio decreased with the increasing of the sample weight.

  凝胶的平衡吸水倍率与测试取样大小有关,平衡吸水倍率随取样质量的增加而减小。

  参考来源 - 光引发AM梯度聚合/胶粒表面接枝聚合及马来酸酐共聚物改性研究
  water absorption - 引用次数：5

  The max water adsorption ratio is 530g/g and the max salt-solution absorption ratio is 58g/g; the rate of water absorption is 8g/min. The keeping-water property and thermal stability of resin are favorable.

  吸水树脂的最大吸水倍率为530g/g,最大吸盐水倍率为58g/g,吸水速率为8g/min,树脂具有良好的保水性和热稳定性。

  参考来源 - 剑麻纤维接枝丙烯酸类单体制备吸水树脂的研究
• water absorbent rate - 引用次数：5

  When absorbed ammonium (nitrogen) gel desorption in water, the absorption can be recovered, and the water absorbent rate can even surpass the original one.

  7、吸铵(氮)凝胶在水中解吸铵的同时,其吸水能力可以得到恢复。 完全释放铵后的凝胶,其吸水倍率甚至会超过未吸附过铵的树脂的吸水倍率。

  参考来源 - 高吸水性树脂与铵离子间的相互作用研究
• absorbency - 引用次数：4

  It turned out that the water-absorbency of the polymer was mostly affected by the crosslinker concentration, but the speed of absorbency was greatly influenced by the ratio of oil to water.

  结果表明两种交联剂对吸水倍率的影响很大，而吸水速度主要受到体系油水比的影响。 制备出了吸水倍率高，吸水速度快的功能性聚合物。

  参考来源 - 反相悬浮聚合制备功能聚合物微球
  absorption rate - 引用次数：3

  The experimental results show that this fiber with low breaking strength and small elongation at break possesses fast water-absorbent velocity,and there is only 15s to be saturated absorption rate,about 90 times.

  实验表明,超吸水纤维的断裂强度低、断裂伸长率小,且呈多分散性;吸水速率极快,浸水15s几乎达到饱和吸水,吸水倍率约90倍。

  参考来源 - 超吸水热防护多层织物的研究
  absoring percentage - 引用次数：1

  参考来源 - 粘土型高吸水性复合材料的制备及其性能研究
• the rate of water-absorbing - 引用次数：2

  参考来源 - 体膨颗粒调剖剂制备及其性能表征方法探讨