钛合金双重退火 titanium alloy double annealing
Uniform equiaxed microstructure was obtained by the deformation at 995℃followed water-quenching and the duplex anneal of 995℃2 h FC+920℃4h FC+570℃6h AC, and the grain size was about 9μm.
对原始魏氏组织进行等轴化处理:在995℃下变形随后水淬,并且经995℃2h FC+920℃4h FC+570℃6h AC双重退火处理,得到分布均匀的等轴组织,晶粒尺寸约为9μm。
参考来源 - TC11钛合金等轴化处理及高温变形行为的研究·2,447,543篇论文数据,部分数据来源于NoteExpress