Semi-solid billets of hypoeutectic high chromium cast iron prepared by inclined cooling plate method were reheated, then thixotropic extruding filled.
本文采用倾斜板冷却体法制备亚共晶高铬铸铁半固态坯料,并对半固态坯料进行二次加热,然后进行触变挤压充型。
参考来源 - 亚共晶高铬铸铁二次加热组织演变及触变挤压充型性能研究·2,447,543篇论文数据,部分数据来源于NoteExpress
分析了亚共晶高铬铸铁半固态浆料进行流变挤压成形后挤压件的力学性能。
The mechanical property of the hypoeutectic high chromium cast iron extrusion samples was analyzed after extruded by semi-solid rheocasting forming.
采用倾斜板冷却体法对亚共晶高铬铸铁进行半固态成形,研究了倾斜板角度对亚共晶高铬铸铁半固态组织的影响规律。
Effects of inclined Angle on semi-solid microstructure of hypoeutectic high cr cast iron prepared by inclined plate cooling method were investigated.
高铬钼抗磨合金本质为亚共晶型高合金白口铸铁。
High chromium-Molybdonum wear-resistant alloys are hypoeutectic white cast iron.