Fe-23%Mo-27.5%Si ternary quasiperitectic alloy was rapidly solidified by 3 m-long drop tube. The diameter of the obtained droplets varies from 100 to 1200 μm.
采用落管无容器处理技术实现了Fe-23%Mo-27.5%Si三元包共晶合金的快速凝固,获得直径为1001 200μm的合金粒子。