The effect of carbon content of the base metal on the welded bond structure, formation mechanism of the "austenitic-rich zone" and "hydrogen-induced disbonding" etc.
研究了母材碳含量对熔合区形态的影响、“富奥氏体区”形成机理和“氢蚀剥离开裂”产生机理等。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在T CS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低,原因是接头热影响区晶粒粗大所致。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低,原因是接头热影响区晶粒粗大所致。