Trilobal nylon 亮光尼龙
Poly Trilobal 轻盈纺
trilobal silicon carbide fibers 三叶形截面sic纤维
trilobal cross 三叶型
Trilobal plate 三叶形钢板
Trilobal Bright 三角亮丝
bright trilobal 有光三叶形
trilobal profiled 三叶异形
trilobal filament 三叶异形丝
The suitable spinning parameters are: temperature 300~306℃, N2 pressure 1.0~1.8MPa, take-up rate 250~450rpm. Under these conditions, trilobal pitch fibers could be obtained with Edo 25~35μm and Dp 0.55~0.60.
合适纺丝工艺为:温度300～306℃、压力1.0～1.8MPa、收丝速率250～450rpm,可得到当量直径为25～35μm、异形度为0.55～0.60的三叶形载银沥青纤维。
参考来源 - 三叶形载银沥青基活性碳纤维的制备与性能·2,447,543篇论文数据，部分数据来源于NoteExpress
Trilobal, swirl-shaped and T-shaped SiC fibers were prepared from precursor polymer.
通过先驱体转化法，制备出三叶形、三折叶形和T形截面碳化硅纤维。
Comparing with the routine PET, the trilobal PET has lower strength and modulus, while its elongation is larger.
与常规圆形丝相比，高伸长异形丝的强度和模量低而断裂伸长率高。
It was found that fibers of circular cross section produce greater cohesion in webs and slivers than do trilobal fibers.
圆形横截面纤维在棉网和棉条中，比三叶形横截面纤维能产生较大的粘著作用。