The sulfide stress cracking is one of the reasons of gas transmission pipeline failure.
硫化物应力腐蚀是引起输气管道失效的主要原因之一。
The resistance of nitrided J55 casing to sulfide stress cracking (SSC) was studied by C-ring testing and three-point bending testing under different conditions.
用应力环腐蚀试验和三(四)点弯曲试验研究了某J 55(即石油套管)渗氮套管在不同试验条件下的腐蚀行为，并和未渗氮套管的抗腐蚀性进行了比较。
It has been proved that these cracks are caused by sulfide stress corrosion cracking (SSCC) through failure analysis and service environment survey.
通过失效分析和管道服役环境调查，证明开裂原因是管道服役期间发生硫化物应力腐蚀开裂(SSCC)。