The results show that the sinterability was advanced by the second phase. While the sintering temperature at 1900℃and the gas pressure of 8Mpa, the relative density of 96% was obtained by adding 50wt%Al_2O_3.
结果表明第二相的加入在一定程度上改善了材料的烧结性能,在1900℃、压力8MPa的条件下,加入50wt%Al_2O_3,烧结体的相对密度为96%。
参考来源 - TiB·2,447,543篇论文数据,部分数据来源于NoteExpress
Sinterability and crystallization behavior of the two types of ferrite composites were compared.
比较了这两种复合材料的结晶性能和烧结性能。
The diamond particles with metallized surface have much the same sinterability, weldability and electrical conductibility (for electroplating)as common metal particles.
这种表面金属化的金刚石颗粒具有一般金属颗粒的可烧结性、可焊接性及表面可导电(可电镀)性。
A new processing preparation that sprays vapoured sol on the surface of heating material is adopted, which not only shortens time, but also gets a relative sinterability powder.
雾化钛酸钡锶溶胶,溶胶粒子在加热基体上快速凝胶,不仅缩短粉体的制备时间,而且制得粉体的粒径均匀。