The hydrophobic rate of silica white was about 80%. when the modifier was silane coupling agent,modification effect was the poorest.
硅烷偶联剂改性效果最差。
参考来源 - 桦甸油页岩残渣制备白炭黑及改性研究The silane content, pH value of silane coupling agent and dipping time of substrates in silane solution influence the quality of silane SAMs. Dipping time always is in the range of 10s～20min.
硅烷偶联剂溶液中硅烷含量、pH值及基片在其中的浸渍时间等条件对硅烷自组装薄膜的质量有影响,一般浸渍时间为10s～20min。
参考来源 - 电磁屏蔽用导电聚吡咯薄膜的研究·2,447,543篇论文数据，部分数据来源于NoteExpress
New silane coupling agent can obviously improve the wetting of porcelain surface.
试制陶瓷偶联剂可以明显改善瓷表面的润湿性。
The results showed that the compatibility of hollow glass bead and resin was improved by adding silane coupling agent.
结果表明，硅烷偶联剂改善了空心玻璃微珠与树脂基体的相容性。
The laboratory and production compounding tests on silane coupling agent containing silica filled tread compound were carried out.
对含硅烷偶联剂的白炭黑填充胎面胶料进行了小配合和大配合试验。