The delamination crack and its effect on the fracture of pipeline steel were investigated by drop-weight tear test(DWTT)at different temperature and micrograph analysis.
通过对管线钢不同温度的落锤撕裂试验和微观断口分析，研究了DWTT试样断口的分层裂纹及其对断裂的影响。
The threshold stress and fracture stress of hydrogen-induced cracking of X80 pipeline steel are studied by constant load test and slow stain rate test.
采用恒载荷和慢应变速率动态拉伸实验方法，测定了X80管道钢在不同充氢条件下的氢致开裂门槛应力和断裂应力。
The method and standard of drop weight tear test were described. It was also discussed how to evaluate the capability of pipeline steel to transit from toughness to fracture by DWTT.
论述了落锤撕裂试验的方法和标准，并对用DWTT来评定管材及其焊接接头的韧脆转化能力进行了探讨。