L10-FePt/BN particle films with strong perpendicular orientation can be obtained after FePt（1nm）/BN（0.25nm）20 multilayer has been vacuum annealed at 700℃for an hour.
FePt （2nm）/ BN （0.5nm）10多层膜和FePt （1nm）/ BN （0.25nm）20多层膜经700℃真空热处理1h后,获得具有良好垂直取向的L10-FePt/BN颗粒膜。
参考来源 - 高磁晶各向异性磁记录介质FePt薄膜的研究In pursuance of high density perpendicular recording, we have investigated the influence of the fabricating conditions on the degree of 001 perpendicular orientation of Pt/Fe multilayer grown on amorphous substrate.
为了实现垂直记录,在非晶基底上生长了Pt/Fe多层膜,研究制备条件对L10-FePt的001垂直取向度的影响。
参考来源 - L1·2,447,543篇论文数据，部分数据来源于NoteExpress
The low-frequency limit in the parallel orientation was higher than that in the perpendicular orientation;
平行方向的低频极限量高于垂直方向的低频极限量；
The high-frequency limit of relative permittivity was the same in the parallel and the perpendicular orientation;
平行方向和垂直方向的介电常数高频极限量相等；
The orientation of the induced hydrofractures arc controlled by the mutually perpendicular orientations of the maximum and minimum principal stress components of in situ stress field.
人工裂隙的方向受地应力场中两个相互垂直的主应力分量—最大主应力和最小主应力的制约。
应用推荐