When the modified neoprene or polyurethane adhesive content in UHMWPE fibers was 6%, the strength of UHMWPE fibers increased 17.2% or 13.9%, respectively.
纤维表面漫胶处理后断裂强力提高,当UHMWPE纤维中改性氯丁胶或聚氨酯粘结剂的含量为6%时,其断裂强力增加17.2%或13.9%。
The physical modification improved melt flowing property and decreased melt viscosity of UHMWPE, the modified product could be processed in special or general facilities.
物理改性提高了UHMWPE的熔体流动性,降低了其熔体黏度,使其能在专用或通用设备上加工成型。
The surface of ultra high molecular weight polyethylene(UHMWPE)fibers was modified by the confected chrome acid treatment solutions.
本文采用不同浓度和温度下的铬酸溶液对超高分子量聚乙烯纤维进行表面处理。