The homopolymer and copolymer of macromonomer acted as transparent polymer materials was discussed .
2.研究探讨了大单体均聚物和共聚物在透明高分子材料方面的应用。
参考来源 - 聚氨酯丙烯酸酯大分子单体及其聚合物的研究The main work of this thesis include:1. Polyoxyethylene fatty acids and excessive unsaturated acid were esterified at 100～110℃, and esterification macromonomer was obtained and the effect of the alcohol polyoxyethylene chain length on esterification was discussed as well.
本论文的主要工作包括：1．在100℃～110℃将脂肪酸聚氧乙烯与过量的不饱和羧酸进行酯化获得酯化大单体，讨论了脂肪醇聚氧乙烯链长对酯化的影响。
参考来源 - 聚丙烯酸高效减水剂的合成及改性研究·2,447,543篇论文数据，部分数据来源于NoteExpress
The influence of rigid chain and flexible chain in macromonomer chain with the performances of materials was analysed.
分析了大单体分子链中刚性链段和柔性链段对材料性能的影响。
The properties of the macromonomer and the functional polymer microspheres have been studied by GPC, spectrophotometer and SEM.
用GPC、分光光度仪和扫描电子显微镜等对合成的聚合物进行了表征。
The main contents were as follows: Two-stage process has been developed to synthesize the macromonomer through surface-modification of silica with polymerizable vinyl groups.
主要研究工作包括以下几个方面： 采用两步法将可聚合的乙烯基单体键接到二氧化硅纳米粒子表面合成大分子单体。